Высококачественная изнашиваемая плита с улучшенными рабочими характеристиками
Общие характеристики изнашиваемых листов DURMAT CP 960:
Плиты DURMAT™ PLATINUM , fabricated with the high performance welding process PTA (Plasma Transferred Arc), is the answer to the increasing demands to improve profitability and
productivity in the heavy industry where we are able to apply special Iron based alloys.
Primary carbides in combination with Ni-, Co and Fe based alloys improve the wear resistance significantly, compared with conventionally welded Cr-carbides.
High wear resistant Fused Tungsten Carbides (FTC) in combination with a Ni-alloy offer excellent protection against sliding, grooving and rolling wear. The Ni-based alloy offers exceptional properties for temperatures up to 500°C.
The PTA process features a metallurgical bond with a dilution limited to 5 – 10%.
A further advantage is the fabrication of thin wear plates which can be used to manufacture weight optimized protective components (e.g. fan blades).
Применение изнашиваемых листов DURMAT CP 960:
Эти покрытия применяются для керамической промышленности, дробления минералов,
горнодобывающей промышленности, вентиляторов и других задач, где существуют
высокие требования к стойкости к износу.
Физические характеристики изнашиваемых листов DURMAT CP 960:
Твердость
62 - 65 HR C
Химический состав 1 слой ( % в массе) изнашиваемых листов DURMAT CP 960:
Fe
Cr
C
Mn
Содержание карбида
баланс
28.8
4.85
0,6
60
Технические данные знашиваемых листов DURMAT CP 960:
Typical / standard dimensions:
Base material
(mm)
Coating (mm)
Total (mm)
Weight (kg/m²)
3
3
6
62
4
3; 4; 6
7; 8; 10
69; 82; 106
5
3; 4; 6
8; 9; 11
77; 90; 115
6
3; 4; 6
9; 10; 12
85; 98; 128
8
3; 4; 6
11; 12; 14
101; 114; 139
10
3; 4; 6
13; 14; 15
117; 130; 155
Plate thickness: 3 mm
Plate dimensions: 2,000 x 1,000 mm *)
Coated area: 1,800 x 800 mm *)
Plate thickness: 4, 5, 6, 8; 10 mm
(alternatively other plate thickness on request)
Plate dimension: 2,500 x 1,250 mm *)
Coated area: 2,300 x 1,100 mm *)
Thinnest coating: 2 mm ± 0.5 mm
*) Другие размеры листа по запросу
Твердость сварного материала:
прим. 60 HRC
Максимальная рабочая температура:
прим. 350 ° C
Пожалуйста следуйте все принятым правилам. Техническая информация, предоставленная в этом техническом листе отображает существующее состояние знаний. Они не являются частью контрактов в качестве гарантии характеристик поставляемых материалов. Следует брать во внимание наши условия поставки и продаж, которые включаются во все контракты.